Saw Welding Flux for Hardfacing Welding
Basic Info
Model No.: welding flux
Product Description
Model NO.: Welding Flux pH: Alkaline Melting Point: >600℃ Function: Protect Weld Metal Manufacturing Method: Agglomerted Basicity: 3.0 Sio2+TiO2: 10-20% Mno+Al2O3: 15-25% S: Less Than 0.06% Kind: Submerged Flux for Rollers Specification: Agglomerated Flux state: Solid Type: Inorganic Chemical Composition: SiO₂=10%-30% Application: Submerged-arc Welding Grain Size: 10-60 Meshes Performance: Good Welding Seam,Easy to Deslag CaF2: 20% Cao+MGO: 35-45% P: Less Than 0.06% Trademark: tw Origin: Laiwu Shandong China Submerged arc welding flux
Standard conforming to:
GB/T12470 F55A4-H08MnMoA
GB/T17854 F308-H0Cr21Ni10 F410-HCr13
Description:
1. It is a kind of high basicity, fluoride-alkaline-type sintered flux, grey round grain.
2. Grain size: 10-60 meshes. Basicity: 3.0.
3. It has a good welding procedure, good weld joint and
Excellent high temperature slag removing. There is no Mn and Si transfer in weld metal.
4. The weld metal have mechanical property and high low temperature impact
Toughness,
5. It is used for bead welding in matching proper wire have good high temperature oxidation Resistance and wear resistance capability.
Cautions:
1. The oil soil, moisture, iron and other foreign substances must be removed from the welding joint.
2. The welding flux must be baked under 300-350ºC for 2 hours.
Compostions(%):
Mechanical performance of deposited metal:
Contact us if you need more details on Welding Flux. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Welding Material、Agglomerated Flux. If these products fail to match your need, please contact us and we would like to provide relevant information.
Standard conforming to:
GB/T12470 F55A4-H08MnMoA
GB/T17854 F308-H0Cr21Ni10 F410-HCr13
Description:
1. It is a kind of high basicity, fluoride-alkaline-type sintered flux, grey round grain.
2. Grain size: 10-60 meshes. Basicity: 3.0.
3. It has a good welding procedure, good weld joint and
Excellent high temperature slag removing. There is no Mn and Si transfer in weld metal.
4. The weld metal have mechanical property and high low temperature impact
Toughness,
5. It is used for bead welding in matching proper wire have good high temperature oxidation Resistance and wear resistance capability.
Cautions:
1. The oil soil, moisture, iron and other foreign substances must be removed from the welding joint.
2. The welding flux must be baked under 300-350ºC for 2 hours.
Compostions(%):
Sio2+Tio2 | Mno+Al2o3 | Cao+Mgo | Caf2 | S | P |
10-20 | 15-25 | 35-45 | 20 | ≤0.06 | ≤0.08 |
Mechanical performance of deposited metal:
Wire | Yield strength(Mpa) | Tensile strength(Mpa) | Elongation | Impact value | |
-20ºC | -40ºC | ||||
H08MnMoa | ≥470 | 550-700 | ≥22% | ≥34 | ≥27 |
Wire | Yield Stress | Tensile Strength | Elongation | AKV(J) |
EM12 | ≥330Mpa | 415-550Mpa | ≥22% | ≥27/-40ºC |
EH14 | ≥400Mpa | 480-660Mpa | ≥22% | ≥27/-40ºC |
Product Categories : Welding Flux
Premium Related Products
Other Products
Hot Products
Polyester Spiral Filter Cloth Made in ChinaWoven Fabric Dryer Mesh BeltPolyester / Nylon Silk Printing Screen Mesh/Belt/ ClothPolyester Forming Mesh BeltPolyeste Car Carpet Felt for CarWater Proof Oil-Proof Polyester Filter Bag for Air FilterationGeo Bag for Construction MaterialPE Water Saving Drip Irrigation Pipe with Round DrippersDouble Layer Geotextile Single Layer Geomembrane Compound GeomembranePet Composite Geotechnological Geomembrane FilmSubmerged Arc Welding Flux for Steel Structure (sj101)Woven 100% Cotton Grey FabricNon Woven Needle Punched Polyester Waterproof Geotextile MaterialNeedle Punch Double Color Jacquard Carpet for Exhibition CarpetWaterproof Anti-Slip Door Mat Carpe with PVC BackingPolyester Non-Woven Plain Red Exhition Carpet